Sintering Processes and Dielectric Properties of Ceramic Material (Ba0.4Ca0.6) Ti4O9

Abstract

Asad Ali*, Abid Zaman, Sarir Uddin and Zafar Iqbal

Dielectric properties of (Ba0.4Ca0.6) Ti4O9 ceramic material prepared by mixed oxide solid state route were studied. X-Ray Diffraction (XRD) showed that the calcined powder of (Ba0.4Ca0.6) Ti4O9 at 900°C crystalizes in the phase of complex peroveskite type. Dielectric properties measurement was carried out by LCR meter at the range of (1 MHz to 100 MHz) and (1 GHz to 2 GHz) frequencies. The εr value of (Ba 0.4 Ca0.6 )Ti4O9 sintered ceramic sample increased with increasing frequency. In the present work, a controlled mixed oxide solid state processing route was used to prepared microwave dielectric material (Ba0.4Ca0.6) Ti4O9 and microwave dielectric properties were measured at relatively lower and higher frequencies.

மறுப்பு: இந்த சுருக்கமானது செயற்கை நுண்ணறிவு கருவிகளைப் பயன்படுத்தி மொழிபெயர்க்கப்பட்டது மற்றும் இன்னும் மதிப்பாய்வு செய்யப்படவில்லை அல்லது சரிபார்க்கப்படவில்லை

இந்தக் கட்டுரையைப் பகிரவும்

குறியிடப்பட்டது

arrow_upward arrow_upward