Comparative Study of Nanobioactive Glass Quaternary System 46S6

Abstract

Mabrouk M, Mostafa AA, Oudadesse H, Wers E, Lucas-Girot A and El-Gohary MI

Different bioactive glass systems have been prepared by sol-gel. However, the production of Na2O-containing bioactive glasses by sol–gel methods has proved to be difficult as the sodium nitrate used in the preparation could be lost from the glass structure during filtration and washing. The aim of this study was to prepare the quaternary system 46S6 of bioactive glass by modified sol-gel techniques with a decrease in the time of gelation. In addition, compare the behaviour of the prepared sol-gel bioactive glass system by its corresponding prepared by melting. The obtained glasses were characterized by using several physicochemical techniques; XRD, FTIR, TEM and SEM beside the effect of the glass particles on the viability of osteoblast like cells (Saos-2). Results show that nanopowders 40-60 nm of 46S6 glass system had been prepared by modified sol-gel (acid-base reaction) method at 600°C in just three days at 600°C. Cell viability by MTT assay confirmed the effectiveness of the prepared nanobioactive glass.

மறுப்பு: இந்த சுருக்கமானது செயற்கை நுண்ணறிவு கருவிகளைப் பயன்படுத்தி மொழிபெயர்க்கப்பட்டது மற்றும் இன்னும் மதிப்பாய்வு செய்யப்படவில்லை அல்லது சரிபார்க்கப்படவில்லை

இந்தக் கட்டுரையைப் பகிரவும்

குறியிடப்பட்டது

arrow_upward arrow_upward